Comparación de metales
| Densidad [kg/dm³] | Conductividad [S*m/mm²] | Resistencia (IACS) [%] | Fuerza máxima [N/mm²] | Coeficiente de resistencia térmica [1E-6/K] | |
| Cu | 8.9 | 58.5 | 100 | 220-270 | 3900-4000 |
| Todos | 2.7 | 36 | 62 | 120-140 | 3900-4100 |
| CCA10% | 3.3 | 37.7 | 65 | 130-180 | 3900-4100 |
| CCA15% | 3.6 | 39.2 | 68 | 170-230 | 3900-4100 |
| HTCCA | 3.6 | 35 | 60 | 230-280 | 3600-3900 |
| ITW | 8.9 | 55 | 95 | 290-370 | 3200-3500 |
| HTW | 8.9 | 54 | 93 | 350-400 | 3200-3600 |
| XHTW | 8.9 | 51 | 88 | 380-450 | 3100-3500 |
| CuNi2 | 8.9 | 20 | 34 | 290-370 | 1000-1600 |
| CuNi6 | 8.9 | 10 | 17 | 310-380 | 500-900 |
| CuNi10 | 8.9 | 6.7 | 11 | 320-380 | 350-400 |
| CuNi23Mn | 8.9 | 3.3 | 6 | 500-550 | 150-200 |
| CuNi44 | 8.9 | 2 | 3 | 520-680 | -80 - 40 |
| CuZn10 | 8.7 | 25.3 | 44 | 340-390 | 1300-1500 |
| CuZn20 | 8.5 | 18.8 | 32 | 390-450 | 1300-1500 |
| CuZn30 | 8.4 | 16 | 27 | 440-540 | 1300-1500 |
| CuZn37 | 8.3 | 15 | 26 | 430-480 | 1300-1500 |
| AgCu1 | 10.5 | 57.5 | 99 | 220-320 | 3800-4000 |
| Ag99.99 | 10.5 | 62.5 | 108 | 170-220 | 3800-4000 |
| Au | 19.3 | 45.5 | 78 | 120-220 | 1400 |
| CuSn6 | 8.8 | 7.5 | 13 | 470-530 | 550-750 |
| AlMg5 | 2.7 | 17 | 29 | 200-300 | 3700-3900 |
| Ms/Ag | 8.5 | 16 | 27 | 440-540 | 1400-1600 |
| Cu/Ag | 8.9 | 58.5 | 100 | 220-270 | 3800-4200 |
| Cu/Ni | 8.9 | 55 | 94 | 250-300 | 3800-4200 |
| 304 | 7.9 | 1.37 | 2 | 850-970 | |
| 316 | 7.9 | 1.33 | 2 | 740-840 | |
| Ni | 8.89 | 11.6 | 20 | 450 - 550 | 5000 - 6000 |